中文摘要: 以甘肃某铬化工场地污染土壤作为处理对象，通过黄铁矿高能球磨活化铁粉制备了铬还原修复材料FeS2/Fe0，考察了该材料对铬污染土壤的还原修复效果，并探究了外场强化修复铬污染土壤的方法。结果表明，FeS2/Fe0修复Cr(Ⅵ)含量为448.1 mg/kg的污染土壤，30 d后去除率达到99.1%，微波场可有效缩短修复周期，机械力—微波场联合作用可将总Cr(Ⅵ)含量为4 995 mg/kg的污染土壤修复降至1.9 mg/kg。
中文关键词: FeS2/Fe0材料 铬污染土壤 微波场 机械力场
Abstract:Taking contaminated soil of a chromium chemical site in Gansu as treatment object, chromium reduction remediation material of FeS2/Fe0 was prepared by high-energy ball milling of pyrite with iron powder. Effect of the material on reduction remediation of chromium-contaminated soil and method of field enhanced remediation of chromium contaminated soil were explored. The results show that removal rate of contaminated soil with Cr(Ⅵ) content of 448.1 mg/kg is 99.1% after 30 days by FeS2/Fe0 remediation. Microwave field can effectively shorten the remediation period, and the combined action of mechanical force and microwave field can reduce contaminated soil with total Cr(Ⅵ) content of 4 995 mg/kg to 1.9 mg/kg.
文章编号： 中图分类号： 文献标志码：
基金项目:国家重点研发计划项目(2018YFC1802204)
| 作者 | 单位 | |
| 李琦 | 中南大学冶金与环境学院 | 183512180@csu.edu.cn |
| 杨卫春* | 中南大学冶金与环境学院 | yang220@csu.edu.cn |
| 李书鹏 | 北京建工环境修复股份有限公司 | |
| 甄胜利 | 北京高能时代环境技术股份有限公司 |
引用文本：
李琦,杨卫春,李书鹏,甄胜利.铬污染土壤修复材料FeS2/Fe0及外场强化修复技术研究[J].有色金属（冶炼部分）,2020(12):89-94.
LI Qi,YANG Wei-chun,LI Shu-peng,ZHEN Sheng-li.Remediation Material of FeS2/Fe0 and Field Enhanced Remediation Technology for Chromium Contaminated Soil[J].Nonferrous Metals (Extractive Metallurgy),2020(12):89-94.
李琦,杨卫春,李书鹏,甄胜利.铬污染土壤修复材料FeS2/Fe0及外场强化修复技术研究[J].有色金属（冶炼部分）,2020(12):89-94.
LI Qi,YANG Wei-chun,LI Shu-peng,ZHEN Sheng-li.Remediation Material of FeS2/Fe0 and Field Enhanced Remediation Technology for Chromium Contaminated Soil[J].Nonferrous Metals (Extractive Metallurgy),2020(12):89-94.
关注微信公众号