中文摘要: 镍铁渣产量大，富含Mg元素，具有较高的回收价值。基于镍铁渣成分及矿相结构等特性，采用常压硫酸浸出法，研究镍铁渣中Mg的浸出反应规律和影响因素。结果表明，在液固比20︰1、浸出温度180 ℃、浸出时间120 min、硫酸质量分数80%的条件下，镁浸出率达到83.73%。该浸出受界面化学反应控制，表观活化能12.72 kJ/mol。
Abstract:Ferronickel slag has high recovery value due to its large amount production and magnesium enrichment. Based on composition and mineral phase structure of ferronickel slag, rules and influencing factors for Mg leaching reaction between ferronickel slag and sulfuric acid solution were studied under atmospheric pressure. The experimental results show that Mg leaching rate is 83.73% under the conditions including L/D=20/1, leaching temperature of 180 ℃, leaching time of 120 min, and mass fraction of sulfuric acid of 80%. Kinetic analysis shows that leaching reaction is controlled by interfacial chemical reaction with apparent activation energy of 12.72 kJ/mol.
文章编号： 中图分类号： 文献标志码：
基金项目:广西重点实验室开放基金项目（GXYSSF1802）
引用文本：
黄治成,高锋,李新生,王开拓,何春林,王友彬,韦悦周.硫酸法常压浸出镍铁渣中镁的正交实验及动力学分析[J].有色金属（冶炼部分）,2020(1):18-21.
huang zhicheng,gao feng,Li xinsheng,Wang kaituo,He chunlin,Wang youbin,Wei yuezhou.Orthogonal Experiments and Kinetic Analysis on Magnesium Leaching from Ferronickel Slag with Sulfuric Acid under Normal Pressure[J].Nonferrous Metals (Extractive Metallurgy),2020(1):18-21.
黄治成,高锋,李新生,王开拓,何春林,王友彬,韦悦周.硫酸法常压浸出镍铁渣中镁的正交实验及动力学分析[J].有色金属（冶炼部分）,2020(1):18-21.
huang zhicheng,gao feng,Li xinsheng,Wang kaituo,He chunlin,Wang youbin,Wei yuezhou.Orthogonal Experiments and Kinetic Analysis on Magnesium Leaching from Ferronickel Slag with Sulfuric Acid under Normal Pressure[J].Nonferrous Metals (Extractive Metallurgy),2020(1):18-21.
关注微信公众号