中文摘要: 采用腐蚀失重、塔菲尔曲线、恒电流放电等方法研究了纯铝在4 mol/L NaOH－乙醇体系以及添加了酒石酸钾钠体系中的腐蚀与电化学行为。结果表明，4 mol/L NaOH＋50%乙醇体系能极大地降低析氢含量，缓蚀率可以达到53.09%，添加酒石酸钾钠后析氢腐蚀进一步降低。
Abstract:The corrosion and electrochemical behaviors of pure aluminum in 4 mol/L NaOH-ethanol-water mixed solutions with or without potassium sodium tartrate addition were investigated by means of weight loss measurement, Tafel polarization curve and galvanostatic discharge. The results show that hydrogen precipitation of aluminum is largely inhibited in 4 mol/L NaOH-50% ethanol solution, and the corrosion inhibition percentage is 53.09%. The hydrogen evolution corrosion is inhibited by the addition of potassium sodium tartrate in 4 mol/L NaOH ethanol-water solution.
keywords: aluminum anode potassium sodium tartrate alkaline ethanol organic solution electrochemical behaviors
文章编号： 中图分类号： 文献标志码：
基金项目:国家自然科学基金资助项目（511340071）
| 作者 | 单位 | |
| 陈启元* | 中南大学 化学化工学院 | hxt450862516@126.com |
| 韩雪涛 | 中南大学 化学化工学院 | |
| 胡慧萍 | 中南大学 |
| Author Name | Affiliation | |
| chenqiyuan | School of Chemistry and Chemical Engineering, Central South University | hxt450862516@126.com |
| hanxuetao | ||
| Hu huiping |
引用文本：
陈启元,韩雪涛,胡慧萍.铝阳极在NaOH-乙醇有机体系中的腐蚀与电化学行为[J].有色金属（冶炼部分）,2012(8):45-47.
chenqiyuan,hanxuetao,Hu huiping.Corrosion and Electrochemical Behaviors of Aluminum Anode in Alkaline Ethanol Organic Solution[J].Nonferrous Metals (Extractive Metallurgy),2012(8):45-47.
陈启元,韩雪涛,胡慧萍.铝阳极在NaOH-乙醇有机体系中的腐蚀与电化学行为[J].有色金属（冶炼部分）,2012(8):45-47.
chenqiyuan,hanxuetao,Hu huiping.Corrosion and Electrochemical Behaviors of Aluminum Anode in Alkaline Ethanol Organic Solution[J].Nonferrous Metals (Extractive Metallurgy),2012(8):45-47.
关注微信公众号