中文摘要: 采用水热法制备了Cd0.5Zn0.5S和掺杂0.4%(摩尔百分数) Mg2 的0.4%Mg/Cd0.5Zn0. 5S固溶体光催化剂。采用UV-Vis、XRD以及电化学等手段对催化剂进行表征，并考查催化剂可见光下分解水制氢的活性。结果表明：Mg2 掺杂提高了Cd0.5Zn0.5S固溶体中光生电子和空穴的分离效率，大大提高了Cd0.5Zn0.5S固溶体光催化制氢的活性。
中文关键词: 光催化 制氢 Mg2 掺杂 Cd0.5Zn0.5S固溶体 可见光
Abstract:Cd0.5Zn0.5S and Mg2 doped (0.4%, mole percent) 0.4%Mg/Cd0.5Zn0.5S solid solution photocatalysts were prepared hydrothermally and characterized by XRD, UV-Vis absorption spectroscope and electrochemistry. Their photo activities were evaluated by production of hydrogen from water under visible light (λ≥420 nm) irradiation. The results show that Mg2 doping improves the separation efficiency of photo-generated electrons and holes in Cd0.5Zn0.5S solid solution, and the visible light photo-catalytic activity of 0.4%Mg/Cd0.5Zn0.5S solid solution was markedly enhanced.
文章编号： 中图分类号： 文献标志码：
基金项目:国家自然科学基金资助项目（21163012）；国家重点基础研究发展规划项目(2009CB220003)；江西省自然科学基金资助项目（2010JZH0096）
| 作者 | 单位 | |
| 程彩虹 | 南昌大学化学系 南昌 330031 | pengshaoqin980@sohu.com |
| 彭绍琴* | 南昌大学化学系 南昌 330031 | pengshaoqin980@sohu.com |
| 李越湘 | 南昌大学化学系 南昌 330031 |
| Author Name | Affiliation | |
| CHENG Cai-hong | Department of Chemistry,Nanchang University | pengshaoqin980@sohu.com |
| PENG Shao-qin | pengshaoqin980@sohu.com | |
| LI Yue-xiang |
引用文本：
程彩虹,彭绍琴,李越湘.Mg2 掺杂Zn0.5Cd0.5S固溶体光催化剂的制备及光解水制氢[J].有色金属（冶炼部分）,2012(8):51-53.
CHENG Cai-hong,PENG Shao-qin,LI Yue-xiang.Preparation of Mg2 Doping Cd0.5Zn0.5S Solid Solution and Its Properties of Splitting Water into Hydrogen[J].Nonferrous Metals (Extractive Metallurgy),2012(8):51-53.
程彩虹,彭绍琴,李越湘.Mg2 掺杂Zn0.5Cd0.5S固溶体光催化剂的制备及光解水制氢[J].有色金属（冶炼部分）,2012(8):51-53.
CHENG Cai-hong,PENG Shao-qin,LI Yue-xiang.Preparation of Mg2 Doping Cd0.5Zn0.5S Solid Solution and Its Properties of Splitting Water into Hydrogen[J].Nonferrous Metals (Extractive Metallurgy),2012(8):51-53.
关注微信公众号