中文摘要: 对高钛渣进行了化学分析和XRD分析，通过一系列工艺流程的试验探索，得到了以高钛渣为原料制备人造金红石TiO2-1的工艺。研究表明，加压浸出、强化焙烧—浸出工艺制备出的人造金红石TiO2品位大于92%，满足YS/T299-2010规定TiO2-1的要求，可为氯化钛白工艺提供优质的人造金红石原料。而直接浸出、还原焙烧—浸出、氧化焙烧—浸出难以满足其要求。
Abstract:High titanium slag was analyzed in terms of its chemical composition and XRD. The process for preparing TiO2-1 grade artificial rutile from high titanium slag was obtained by means of a series of exploration tests. The results show that pressure leaching and enhanced roasting-leaching process could prepare artificial rutile with over 92% TiO2 content from high-titanium slag, which meets TiO2-1 requirement of YS/T299-2010, as a result, it can be used as the superior raw materials for chloride titanium white production. In addition, some other methods were studied, such as direct leaching, reducing roasting-leaching, oxidizing roasting-leaching and so on, through which the grade of TiO2 was less than 90%.
文章编号： 中图分类号： 文献标志码：
基金项目:国家高技术研究发展计划（2006AA06Z128）
| Author Name | Affiliation | |
| Jiang Wei | Beijing General Research Institute of Mining Metallurgy | jiangwei@bgrimm.com.cn |
| Jiang Xun-xiong | ||
| Wang Sheng-dong | ||
| Fan Yan-qing | ||
| Liu Wei |
引用文本：
蒋伟,蒋训雄,汪胜东,范艳青,刘巍.高钛渣制备人造金红石工艺研究[J].有色金属（冶炼部分）,2012(3):22-25.
Jiang Wei,Jiang Xun-xiong,Wang Sheng-dong,Fan Yan-qing,Liu Wei.Study on Preparing Artificial Rutile from High Titanium Slag[J].Nonferrous Metals (Extractive Metallurgy),2012(3):22-25.
蒋伟,蒋训雄,汪胜东,范艳青,刘巍.高钛渣制备人造金红石工艺研究[J].有色金属（冶炼部分）,2012(3):22-25.
Jiang Wei,Jiang Xun-xiong,Wang Sheng-dong,Fan Yan-qing,Liu Wei.Study on Preparing Artificial Rutile from High Titanium Slag[J].Nonferrous Metals (Extractive Metallurgy),2012(3):22-25.
关注微信公众号