中文摘要: 以钴中间品为原料，在鼓风氧化条件下，采用硫酸亚铁浸出钴中间品的钴，Fe2+能将Co3+还原为Co2+，同时，Fe2+与氧气作用生成FeOOH时产生酸，产生的酸可进一步浸出钴中间品。较优的工艺条件为：温度80 ℃、Fe/Co摩尔比1.05、液固比8、浸出时间3 h、鼓风量8 L/min、电位285 mV，在此条件下，Co浸出率达到99.7%。该方法无需加酸、碱、还原试剂，环境友好，为钴中间品原料的浸出探索了一条新的解决路径。
Abstract:Cobalt was leached from cobalt intermediate under condition of blast oxidation with ferrous sulfate. Fe2+ reduces Co3+ to Co2+, and Fe2+ reacts with oxygen to form FeOOH, meanwhile producing acid, which can further leach cobalt intermediate. Co leaching rate is 99.7% under the optimum conditions including temperature of 80 ℃, Fe/Co molar ratio of 1.05, L/S of 8, leaching time of 3h, air blowing volume rate of 8 L/min, and potential of 285 mV. This method is eco-friendly without using of acid, alkali, or reductant. It provides a new solution for leaching of cobalt intermediate and removing iron from ferrous leaching solution.
keywords: cobalt intermediate ferrous oxygenation acid free leaching
文章编号： 中图分类号： 文献标志码：
基金项目:江西省赣州市科技计划资助项目（赣市科发[2018]50号）；江西省重点新产品计划项目（20111CX18600）
| 作者 | 单位 | |
| 熊以俊 | 赣州逸豪优美科实业有限公司 | yijun.xiong@gzhongsheng.com |
| 陈斌 | 赣州逸豪优美科实业有限公司 | |
| 谢欣旭 | 赣州逸豪优美科实业有限公司 | |
| 罗旋 | 赣州逸豪优美科实业有限公司 | |
| 许用华* | 赣州逸豪优美科实业有限公司 | sys@gzhongsheng.com |
引用文本：
熊以俊,陈斌,谢欣旭,罗旋,许用华.亚铁离子加氧浸出钴中间品的钴[J].有色金属（冶炼部分）,2022(1):14-19.
XIONG Yi-jun,CHEN Bing,XIE Xin-xu,LUO Xuan,XU Yong-hua.Leaching of Cobalt from Cobalt Intermediate with Ferrous Ion and Oxygen[J].Nonferrous Metals (Extractive Metallurgy),2022(1):14-19.
熊以俊,陈斌,谢欣旭,罗旋,许用华.亚铁离子加氧浸出钴中间品的钴[J].有色金属（冶炼部分）,2022(1):14-19.
XIONG Yi-jun,CHEN Bing,XIE Xin-xu,LUO Xuan,XU Yong-hua.Leaching of Cobalt from Cobalt Intermediate with Ferrous Ion and Oxygen[J].Nonferrous Metals (Extractive Metallurgy),2022(1):14-19.
关注微信公众号