中文摘要: 氢氧化镁是一种应用广泛的新型绿色环保材料，如何低成本制备高品质氢氧化镁引起广泛关注。以水氯镁石和高钙菱镁石为原料，采用湿法冶金工艺制取氢氧化镁，探讨反应时间、反应温度、水氯镁石浓度、煅烧后物料的粒度等对氢氧化镁纯度的影响。结果表明，在80 ℃恒温水浴，反应时间6 h，水氯镁石浓度5%，煅后菱镁石粒度-45 μm条件下得到的氢氧化镁沉淀纯度可达94.89%，主要物相为Mg(OH)2和CaO。
Abstract:As a new green and environmental protection material, magnesium hydroxide is widely used. How to prepare high-quality magnesium hydroxide at low cost has attracted wide attention. Bischofite and high-calcium magnesite were used as raw materials to prepare magnesium hydroxide by hydrometallurgical process. Influences of reaction time, reaction temperature, bischofite concentration, and particle size of calcined material on purity of magnesium hydroxide were discussed. The results show that magnesium hydroxide precipitate with purity of 94.89% and main phase of Mg (OH)2 and CaO is obtained under the conditions including thermostatic waterbath temperature of 80 ℃, reaction time of 6 h, bischofite concentration of 5%, and particle size of calcined magnesite of —45 μm.
文章编号： 中图分类号： 文献标志码：
基金项目:国家重点研发计划项目（2020YFC1909300）；辽宁省教育厅科学研究经费项目（L2020003）；辽宁省化学助剂合成与分离重点实验室项目（ZJNK2012）；营口理工学院创新团队项目（TD201901）
| 作者 | 单位 | |
| 郭丽莉* | 辽宁省化学助剂合成与分离重点实验室,营口理工学院 | 458321315@qq.com |
| 李振 | 辽宁省化学助剂合成与分离重点实验室,营口理工学院 | |
| 王晓民 | 辽宁省化学助剂合成与分离重点实验室,营口理工学院 | |
| 王耀武 | 东北大学 | |
| 王有为 | 营口理工学院 |
引用文本：
郭丽莉,李振,王晓民,王耀武,王有为.水氯镁石和高钙菱镁石制备氢氧化镁[J].有色金属（冶炼部分）,2022(1):103-107.
GUO Li-li,LI Zhen,WANG Xiao-min,WANG Yao-wu,WANG You-wei.Preparation of Magnesium Hydroxide from Bischofite and High-calcium Magnesite[J].Nonferrous Metals (Extractive Metallurgy),2022(1):103-107.
郭丽莉,李振,王晓民,王耀武,王有为.水氯镁石和高钙菱镁石制备氢氧化镁[J].有色金属（冶炼部分）,2022(1):103-107.
GUO Li-li,LI Zhen,WANG Xiao-min,WANG Yao-wu,WANG You-wei.Preparation of Magnesium Hydroxide from Bischofite and High-calcium Magnesite[J].Nonferrous Metals (Extractive Metallurgy),2022(1):103-107.
关注微信公众号