中文摘要: 采用焙烧—酸浸的方法从某Li2O品位为0.64%的黏土型锂矿中浸出锂，考察了焙烧时间和焙烧温度对Li2O浸出率的影响，利用正交试验研究了酸浸工艺中浸出温度和时间、硫酸浓度和液固比对Li2O浸出率的影响。结果表明，黏土型锂矿在600 ℃焙烧30 min后，锂焙烧渣在浸出温度90 ℃、浸出时间30 min、硫酸浓度为1.5 mol/L、浸出液固比为6的条件下搅拌浸出，Li2O浸出率最高达92.97%，浸出效果良好。
Abstract:Lithium was leached from clay-type lithium ore with Li2O grade of 0.64% by roasting-acid leaching. Effects of roasting time and temperature on Li2O leaching rate were investigated. Effects of leaching temperature and time, sulfuric acid concentration, and ratio of liquid to solid (L/S) on Li2O leaching rate in acid leaching process were investigated by orthogonal test. The results show that Li2O leaching rate is 92.97% under the optimum conditions including roasting time of 30 min, roasting temperature of 600 ℃, leaching temperature of 90 ℃, leaching time of 30 min, sulfuric acid concentration of 1.5 mol/L, and L/S=6.
keywords: clay- type lithium ore lithium roasting leaching
文章编号： 中图分类号： 文献标志码：
基金项目:中国地质调查局公益性地质调查项目（DD20211236）
| 作者 | 单位 | |
| 徐璐* | 中国地质科学院矿产综合利用研究所 | xlu@mail.cgs.gov.cn |
| 惠博 | 中国地质科学院矿产综合利用研究所 | |
| 龚大兴 | 中国地质科学院矿产综合利用研究所 | |
| 赖杨 | 中国地质科学院矿产综合利用研究所 | |
| 田恩源 | 中国地质科学院矿产综合利用研究所 |
引用文本：
徐璐,惠博,龚大兴,赖杨,田恩源.从黏土型锂矿中高效浸出锂的研究[J].有色金属（冶炼部分）,2021(9):37-40.
XU Lu,HUI Bo,GONG Da-xing,LAI Yang,TIAN En-yuan.Study on High-efficient Leaching of Lithium from Clay-type Lithium Ore[J].Nonferrous Metals (Extractive Metallurgy),2021(9):37-40.
徐璐,惠博,龚大兴,赖杨,田恩源.从黏土型锂矿中高效浸出锂的研究[J].有色金属（冶炼部分）,2021(9):37-40.
XU Lu,HUI Bo,GONG Da-xing,LAI Yang,TIAN En-yuan.Study on High-efficient Leaching of Lithium from Clay-type Lithium Ore[J].Nonferrous Metals (Extractive Metallurgy),2021(9):37-40.
关注微信公众号