中文摘要: 采用等温饱和法研究了静置和搅拌状态对TiO2在Na3AlF6-AlF3-CaF2熔盐体系中的溶解速率及溶解量的影响，分别对空冷和水淬处理的熔盐样品进行X射线衍射分析。结果表明：熔盐温度为960 ℃时，静置状态下，TiO2的溶解量随溶解时间的延长而增加，溶解120 min时的溶解量为2.33%；搅拌条件下，提高了溶解速率，溶解120 min时的溶解量为5.33%；XRD分析表明二氧化钛在熔盐体系中以TiO2相存在。
Abstract:Effects of static condition and stirring condition on dissolution rate and amount of TiO2 in Na3AlF6-AlF3-CaF2 molten salt system were studied by isothermal saturation method. The samples of molten salt treated by air cooling and water quenching were analyzed by X-ray diffraction. The results show that TiO2 dissolved amount under static condition rises with prolongation of dissolution time, and dissolution amount is 2.33% at 120 min when the temperature of molten salt is 960 ℃ while, it is 5.33% under stirring condition. XRD analysis shows that titanium dioxide exists in form of TiO2 phase in molten salt system.
keywords: molten salt TiO2 stirring dissolved amount
文章编号： 中图分类号： 文献标志码：
基金项目:贵州省普通高等学校科技拔尖人才支持计划项目（黔教合KY字[2016]062）
| 作者 | 单位 | |
| 余娅红 | 贵州师范大学 材料与建筑工程学院 | 2442547026@qq.com |
| 张念炳* | 贵州师范大学 材料与建筑工程学院 | zhangnianbing@126.com |
| 耿芃 | 贵州师范大学 材料与建筑工程学院 | |
| 周军 | 贵州师范大学 材料与建筑工程学院 |
引用文本：
余娅红,张念炳,耿芃,周军.强制搅拌对Na3AlF6-AlF3-CaF2熔盐体系中TiO2溶解的影响[J].有色金属（冶炼部分）,2020(12):31-35.
YU Ya-hong,ZHANG Nian-bing,GENG Peng,ZHOU Jun.Effect of Forced Stirring on Dissolution of TiO2 in Na3AlF6-AlF3-CaF2 Molten Salt System[J].Nonferrous Metals (Extractive Metallurgy),2020(12):31-35.
余娅红,张念炳,耿芃,周军.强制搅拌对Na3AlF6-AlF3-CaF2熔盐体系中TiO2溶解的影响[J].有色金属（冶炼部分）,2020(12):31-35.
YU Ya-hong,ZHANG Nian-bing,GENG Peng,ZHOU Jun.Effect of Forced Stirring on Dissolution of TiO2 in Na3AlF6-AlF3-CaF2 Molten Salt System[J].Nonferrous Metals (Extractive Metallurgy),2020(12):31-35.
关注微信公众号