中文摘要: 焙烧氰化提金工艺产出大量的尾渣，为充分浸出尾渣中的铁，降低铁对金的包裹，采用硫酸熟化法对尾渣中的Fe2O3的分解进行了研究，主要研究了硫酸熟化过程中硫酸加入量对渣中铁的物相影响规律，浓硫酸加入量、熟化时间对铁浸出率的影响规律。结果表明：在100 ℃、浓硫酸熟化氰化尾渣1 h、硫酸与尾渣质量比0.6时，渣中铁的浸出率达到82.64%，主要是熟化过程中渣中难溶的Fe2O3转变为易溶的HFe(SO4)2?4H2O所致。
Abstract:A large amount of cyanide residue was produced by gold concentrate roasting-cyaniding process. In order to leach iron from cyanide residue and reduce iron entrapment on gold, decomposition of Fe2O3 in cyanide residue was studied by sulfuric acid curing method. Influence of sulfuric acid dosage on phase of iron in cyanide residue during sulfuric acid curing process, and influences of dosage of concentrated sulfuric acid and curing time on iron leaching rate were investigated. The results show that iron leaching rate is 82.64% when residue is cured at 100 ℃ for 1 h and mass ratio of sulfuric acid to tailings is 0.6. The high leaching rate of iron is mainly due to transformation of refractory Fe2O3 into soluble HFe(SO4)2?4H2O in residue during curing process.
keywords: cyanide residue curing iron oxide leaching
文章编号： 中图分类号： 文献标志码：
基金项目:国家自然科学基金资助项目（51974221）；陕西省教育厅重点实验室科学研究计划项目（17JS067）
引用文本：
马红周,王丁丁,王耀宁,党晓娥,王碧侠.硫酸熟化法浸出焙烧氰化尾渣中的铁[J].有色金属（冶炼部分）,2020(10):19-22.
MA Hong-zhou,WANG Ding-ding,WANG Yao-ning,DANG Xiao-e,WANG Bi-xia.Leaching of Iron from Roasting Cyanide Tailings by Sulfuric Acid Curing Method[J].Nonferrous Metals (Extractive Metallurgy),2020(10):19-22.
马红周,王丁丁,王耀宁,党晓娥,王碧侠.硫酸熟化法浸出焙烧氰化尾渣中的铁[J].有色金属（冶炼部分）,2020(10):19-22.
MA Hong-zhou,WANG Ding-ding,WANG Yao-ning,DANG Xiao-e,WANG Bi-xia.Leaching of Iron from Roasting Cyanide Tailings by Sulfuric Acid Curing Method[J].Nonferrous Metals (Extractive Metallurgy),2020(10):19-22.
关注微信公众号