中文摘要: 采用氧压酸浸工艺处理高硅富铟渣，系统考察了始酸浓度、氧分压、反应温度、反应时间和液固比等对浸铟沉硅效果的影响。试验结果表明：在始酸浓度120 g/L、液固比5:1、釜内压力0.6 MPa、反应温度160 ℃、反应时间1.5 h的条件下，铟浸出率高达97.3%，硅沉淀率为98.5%；高压高温工艺能抑制富铟渣酸浸过程中硅胶的形成，浸出矿浆的过滤性能良好。
Abstract:Indium-rich slag was treated by oxygen pressure acid leaching process. Effects of initial acid concentration, pressure in autoclave, temperature, time and L/S on indium leaching and silicon precipitation were investigated. The results show that indium leaching rate is 97.3% and silicon precipitation rate is 98.5% under the conditions including initial acid concentration of 120 g/L, L/S=5/1, pressure in autoclave of 0.6 MPa, reaction temperature of 160 ℃,and reaction time of 1.5 h. High pressure and high temperature process can inhibit formation of silica gel during acid leaching of indium-rich slag, and leaching slurry has good filtration performance.
文章编号： 中图分类号： 文献标志码：
基金项目:国家自然科学基金青年基金资助项目(51704133)；江西省省级研究生教改研究项目(JXYJG-2018-127)；江西理工大学清江青年英才支持计划项目(JXUSTQJBJ2017004)；江西理工大学校级大学生创新创业训练计划项目（DC2018-015）
| 作者 | 单位 | |
| 贺山明* | 江西理工大学 冶金工程学院 | heshanming200809@163.com |
| 吴鑫 | 江西理工大学 冶金工程学院 | heshanming200809@163.com |
| 梁勇 | 江西理工大学 冶金工程学院 | |
| 廖春发 | 江西理工大学 冶金工程学院 |
引用文本：
贺山明,吴鑫,梁勇,廖春发.高硅富铟渣氧压酸浸过程中浸铟沉硅的研究[J].有色金属（冶炼部分）,2020(1):56-59.
Shanming He,Xin Wu,Yong Liang,Chunfa Liao.Study on Indium Leaching and Silicon Precipitation from Indium-Rich High-Silicon Bearing Slag during Oxygen Pressure Acid Leaching[J].Nonferrous Metals (Extractive Metallurgy),2020(1):56-59.
贺山明,吴鑫,梁勇,廖春发.高硅富铟渣氧压酸浸过程中浸铟沉硅的研究[J].有色金属（冶炼部分）,2020(1):56-59.
Shanming He,Xin Wu,Yong Liang,Chunfa Liao.Study on Indium Leaching and Silicon Precipitation from Indium-Rich High-Silicon Bearing Slag during Oxygen Pressure Acid Leaching[J].Nonferrous Metals (Extractive Metallurgy),2020(1):56-59.
关注微信公众号