中文摘要: 针对锑工业生产过程中产生大量硫化锑渣的物料特性，通过理论分析研究，采用真空蒸发的方法处理硫化锑渣，并考察了物料粒径、体系压强、蒸发时间和蒸发温度对硫化锑渣蒸发率的影响。结果表明，在物料粒径0.106~0.075 mm、体系压强50 Pa、蒸发时间30 min、蒸发温度923 K的条件下，蒸余物中锑含量降至0.2%，硫化锑渣的蒸发率为27.9%，锑分离效率为98.6%。
Abstract:Antimony sulfide slag from antimony industrial processes was treated by vacuum evaporation to recover antimony based on characteristics of antimony sulfide slag and theoretical analysis. Effects of particle size of materials, system pressure, evaporation time, and evaporation temperature on evaporation ratio of antimony sulfide slag were investigated. The results show that evaporation ratio is 27.9% and antimony content in distilland reduces to 0.2% with antimony separation efficiency of 98.6% under the conditions including particle size of 0.106~0.075 mm, evaporation temperature of 923 K, evaporation time of 30 min, and system pressure of 50 Pa.
文章编号： 中图分类号： 文献标志码：
基金项目:云南省基础研究计划项目（2017FA031）；中央引导地方科技发展专项资金项目；科研院所技术开发研究专项基金（2018DC010）
| Author Name | Affiliation | |
| Bao zhi-qun | Kunming Metallurgical institute | 924263330@qq.com |
| QIU Ke-qiang |
引用文本：
包稚群,丘克强.真空蒸发法从硫化锑渣中回收锑[J].有色金属（冶炼部分）,2019(3):11-14.
Bao zhi-qun,QIU Ke-qiang.Antimony Recovery from Antimony Sulfide Slag with Vacuum Evaporation[J].Nonferrous Metals (Extractive Metallurgy),2019(3):11-14.
包稚群,丘克强.真空蒸发法从硫化锑渣中回收锑[J].有色金属（冶炼部分）,2019(3):11-14.
Bao zhi-qun,QIU Ke-qiang.Antimony Recovery from Antimony Sulfide Slag with Vacuum Evaporation[J].Nonferrous Metals (Extractive Metallurgy),2019(3):11-14.
关注微信公众号