中文摘要: 探究CL-P204萃淋树脂对溶液中V(IV)的吸附效果。考察溶液pH、反应时间、初始浓度、温度对钒吸附容量的影响，并对吸附过程进行了动力学和热力学分析。结果表明，CL-P204萃淋树脂在298 K、pH=1.6的条件下，吸附8 h即可达到平衡，对V(IV)的最大吸附容量为34.2 mg/g。树脂循环使用4次后对钒依然有良好的吸附效果。CL-P204萃淋树脂对钒的吸附过程符合准二级动力学方程和Langmuir等温吸附方程，是吸热熵增加的自发反应。
Abstract:Adsorption performance of CL-P204 levextrel resin for V(IV) was studied. The effects of pH value of solution, oscillation time, initial vanadium concentration, and temperature on adsorption capacity were investigated. Adsorption thermodynamics and kinetics as well as isothermal adsorption model were analyzed. The results show that adsorption of CL-P204 resins can achieve equilibrium after 8 h with saturation adsorption capacity of 34.2 mg/g for V(IV) at 298 K and pH=1.6. Levextrel resin can maintain good absorption capacity after 4 cycles. Adsorption of V(IV) on levextrel resin is in accordance with pseudo-second order kinetic equation and Langmuir isothermal adsorption equation, and adsorption process is a spontaneous reaction from endothermic entropy increase.
文章编号： 中图分类号： 文献标志码：
基金项目:国家自然科学基金资助项目（51404177）；国家科技支撑计划项目（2015BAB03B05）
| 作者 | 单位 | |
| 郑汝伟 | 武汉理工大学 资源与环境工程学院 | zhruwei@126.com |
| 包申旭* | 武汉理工大学 资源与环境工程学院 钒资源高效利用湖北省协同创新中心 | sxbao@whut.edu.cn |
| 张一敏 | 武汉科技大学 资源与环境工程学院；钒资源高效利用湖北省协同创新中心；武汉理工大学 资源与环境工程学院 | zym126135@126.com |
| 杨晓 | 武汉理工大学 资源与环境工程学院 |
引用文本：
郑汝伟,包申旭,张一敏,杨晓.CL-P204萃淋树脂对溶液中钒的吸附性能研究[J].有色金属（冶炼部分）,2017(1):45-48.
Zheng Ruwei,Bao Shenxu,Zhang Yimin,YANG Xiao.Study on Adsorption Properties of CL-P204 Levextrel Resin for Vanadium(Ⅳ)[J].Nonferrous Metals (Extractive Metallurgy),2017(1):45-48.
郑汝伟,包申旭,张一敏,杨晓.CL-P204萃淋树脂对溶液中钒的吸附性能研究[J].有色金属（冶炼部分）,2017(1):45-48.
Zheng Ruwei,Bao Shenxu,Zhang Yimin,YANG Xiao.Study on Adsorption Properties of CL-P204 Levextrel Resin for Vanadium(Ⅳ)[J].Nonferrous Metals (Extractive Metallurgy),2017(1):45-48.
关注微信公众号