中文摘要: 对黄铵铁矾渣的组成结构及其焙烧酸浸行为进行研究，以达到使渣中的铟、锌和铁得到高效分离和利用的目的。由MLA分析推测黄铵铁矾渣的结构式为NH4Fe3(SO4)2(OH)6，渣中的铁主要包含在黄铵铁矾结构中，锌主要包含在水锌矾Zn[SO4]?H2O结构中。在680~720 ℃焙烧1.5 h后酸浸，铟的浸出率大于82%，锌的浸出率大于95%，铁的浸出率小于10%，实现了黄铵铁矾渣中的锌、铟和铁的有效分离。
Abstract:Composition, structure, roasting, and acid leaching of ammonium jarosite residue were investigated to achieve the goal of effective separation and usage of In/Zn and Fe in residue. The analysis results of MLA show that structure of jarosite residue is NH4Fe3(SO4)2(OH)6, Fe is mainly in structure of NH4Fe3(SO4)2(OH)6, and Zn is mainly in structure of Zn[SO4]?H2O. Acid leaching rate of In, Zn, and Fe is 82% above, 95% above, and 10% below respectively after roasted at 680~720 ℃ for 1.5 h. In, Zn, and Fe are efficiently separated from ammonium jarosite residue.
keywords: ammonium jarosite residue roasting acid leaching indium zinc
文章编号： 中图分类号：TF832 文献标志码：
基金项目:广东省科技计划项目（2015A020215018）；广东省自然科学基金项目（2016A030313801）
| 作者 | 单位 | |
| 高丽霞* | 广东省稀有金属研究所 | gaolixia_glx@yeah.net |
| 戴子林 | 广东省稀有金属研究所 | |
| 张魁芳 | 广东省稀有金属研究所 | |
| 刘志强 | 广东省稀有金属研究所 | |
| 董颖超 | 中国农业科学院饲料研究所 |
| Author Name | Affiliation | |
| GAO Lixia | Guangdong Institute of Rare Metals | gaolixia_glx@yeah.net |
| DAI Zilin | ||
| Zhang Kuifang | ||
| Liu Zhiqiang | ||
| Dong Yingchao |
引用文本：
高丽霞,戴子林,张魁芳,刘志强,董颖超.黄铵铁矾渣的焙烧酸浸行为研究[J].有色金属（冶炼部分）,2016(10):9-11.
GAO Lixia,DAI Zilin,Zhang Kuifang,Liu Zhiqiang,Dong Yingchao.Study on Roasting and Acid Leaching of Ammonium Jarosite Residue[J].Nonferrous Metals (Extractive Metallurgy),2016(10):9-11.
高丽霞,戴子林,张魁芳,刘志强,董颖超.黄铵铁矾渣的焙烧酸浸行为研究[J].有色金属（冶炼部分）,2016(10):9-11.
GAO Lixia,DAI Zilin,Zhang Kuifang,Liu Zhiqiang,Dong Yingchao.Study on Roasting and Acid Leaching of Ammonium Jarosite Residue[J].Nonferrous Metals (Extractive Metallurgy),2016(10):9-11.
关注微信公众号