中文摘要: 用去离子水以及1 mol/L KCl溶液测试自制溶液电导在线检测系统的稳定性和自制电极的电导池常数。结果表明，测试的数据稳定可靠，得到电导池常数为136 cm-1。测量了Na2O浓度为110 g/L、分子比为1.33的铝酸钠溶液均相分解时溶液电导随时间的变化规律，结合溶液等效电路分析，初步阐明了铝酸钠溶液分解各个阶段的特征。
Abstract:The stability of homemade online testing system of solution conductivity and constant of electrode conductivity cell were tested by laboratory water and 1 mol/L KCl. The results show that the testing data is stable and reliable, and the constant of electrode conductivity cell is 136 cm-1. The conductivity of sodium aluminate solution (c(Na2O)=110 g/L, αk=1.33), which changes over time when decomposed homogeneously, is measured. The characteristics at each stage of decomposition are illustrated analysis on equivalent circuit of solution.
keywords: on-line conductivity detection sodium aluminate solution homogeneous decomposition conductivity
文章编号： 中图分类号：0645.5 文献标志码：
基金项目:国家自然科学基金资助项目(51374251)
| 作者 | 单位 | |
| 李俊 | 中南大学 化学化工学院 | csuljmetal@sina.com |
| 尹周澜* | 中南大学 化学化工学院 | xhli@csu.edu.cn |
| 丁治英 | 中南大学 化学化工学院 | |
| 张平民 | 中南大学 化学化工学院 |
| Author Name | Affiliation | |
| LI Jun | College of Chemistry and Chemical Engineering,Central South University | csuljmetal@sina.com |
| YIN Zhou-Lan | xhli@csu.edu.cn | |
| DING Zhi-Ying | ||
| ZHANG Ping-Min |
引用文本：
李俊,尹周澜,丁治英,张平民.铝酸钠溶液均相分解过程的电导法研究[J].有色金属（冶炼部分）,2015(11):17-20.
LI Jun,YIN Zhou-Lan,DING Zhi-Ying,ZHANG Ping-Min.Study on Homogeneous Decomposition of Sodium Aluminate Solution by Conductometry[J].Nonferrous Metals (Extractive Metallurgy),2015(11):17-20.
李俊,尹周澜,丁治英,张平民.铝酸钠溶液均相分解过程的电导法研究[J].有色金属（冶炼部分）,2015(11):17-20.
LI Jun,YIN Zhou-Lan,DING Zhi-Ying,ZHANG Ping-Min.Study on Homogeneous Decomposition of Sodium Aluminate Solution by Conductometry[J].Nonferrous Metals (Extractive Metallurgy),2015(11):17-20.
关注微信公众号