中文摘要: 以N902为萃取剂，从废弃印刷线路板氨性浸出液中萃取回收铜，研究萃取剂浓度、相比(O/A)、萃原液初始pH和时间对铜萃取率的影响。结果表明，室温下N902萃取铜最优条件为：萃取剂浓度15%、O/A=1︰2、料液初始pH=10、萃取时间2.5 min。在此条件下Cu2+萃取率达98.62%，用2 mol/L硫酸溶液对负载有机相进行一级反萃4 min，Cu2+反萃率达89.91%，其溶液可满足电积提铜的要求。
Abstract:Copper was extracted with N902 from ammoniacal leaching solution of waste printed circuit boards. The effects of extraction agent concentration, extraction phase ratio (O/A), initial pH value of extraction solution and extraction time on copper extraction rate were investigated. The results show that copper extraction rate is 98.62% under the optimum conditions including extractant concentration of 15%, O/A=1︰2, initial pH of 10, and extraction time of 2.5 min. Stripping rate of copper is 89.91% with 2 mol/L sulfuric acid solution for 4 min. The solution can meet the requirement of copper electrowinning.
文章编号： 中图分类号： 文献标志码：
基金项目:湖北省高等学校青年教师深入企业行动计划项目(XD2012604)
| 作者 | 单位 | |
| 康立武* | 湖北工程职业学院 | linkkangliwu@163.com |
| 王青云 | 湖北工程职业学院 | |
| 邹燕飞 | 方大特钢科技股份有限公司 |
| Author Name | Affiliation | |
| KANG Li-wu | Hubei Engineering Institute | linkkangliwu@163.com |
| WANG Qing-yun | ||
| ZOU Yan-fei |
引用文本：
康立武,王青云,邹燕飞.用N902萃取废印刷线路板中的铜[J].有色金属（冶炼部分）,2015(10):30-33.
KANG Li-wu,WANG Qing-yun,ZOU Yan-fei.Solvent Extraction of Copper from Waste Printed Circuit Boards with N902[J].Nonferrous Metals (Extractive Metallurgy),2015(10):30-33.
康立武,王青云,邹燕飞.用N902萃取废印刷线路板中的铜[J].有色金属（冶炼部分）,2015(10):30-33.
KANG Li-wu,WANG Qing-yun,ZOU Yan-fei.Solvent Extraction of Copper from Waste Printed Circuit Boards with N902[J].Nonferrous Metals (Extractive Metallurgy),2015(10):30-33.
关注微信公众号