中文摘要: 考察了过硫酸钠浓度、硫酸加入量、搅拌速度、温度和固液比对过硫酸钠直接回收废电路板金属富集体中铜的影响。结果表明，增加过硫酸钠浓度、搅拌速度和升高温度有利于铜的回收。在45 ℃、固液比0.004(g/mL)、搅拌速度500 r/min、过硫酸钠浓度0.2 mol/L、时间60 min的条件下，铜的回收率达96.5%。
Abstract:The effects of concentration of sodium persulfate, amount of sulfuric acid, stirring speed, temperature and ratio of solid to liquid on recovery of copper from metal concentrates of waste printed circuit boards with sodium persulfate were investigated. The results show that increasing of concentration of sodium persulfate, stirring speed and temperature facilitates copper recovery. Copper recovery is 96.5% under the optimum conditions including temperature of 45 ℃, ratio of solid to liquid of 0.004(g/mL), stirring speed of 500 r/min, concentration of sodium persulfate of 0.2 mol/L, and leaching time of 60 min.
keywords: wasted circuit boards copper sodium persulfate
文章编号： 中图分类号： 文献标志码：
基金项目:河南省高等学校重点科研项目（15A610006）
| 作者 | 单位 | |
| 王治科* | 河南师范大学环境学院 河南省环境污染控制重点实验室 | wzk@htu.cn |
| 武海丽 | 河南师范大学环境学院 河南省环境污染控制重点实验室 | |
| 叶存玲 | 河南师范大学环境学院 河南省环境污染控制重点实验室 | |
| 范顺利 | 河南师范大学环境学院 河南省环境污染控制重点实验室 |
引用文本：
王治科,武海丽,叶存玲,范顺利.过硫酸钠直接回收废电路板金属富集体中的铜[J].有色金属（冶炼部分）,2015(10):34-36.
Wang Zhi-ke,Wu Hai-li,Ye Cun-ling,Fan Shun-li.Direct Recovery of Copper from Metal Concentrates of Waste Printed Circuit Boards with Sodium Persulfate[J].Nonferrous Metals (Extractive Metallurgy),2015(10):34-36.
王治科,武海丽,叶存玲,范顺利.过硫酸钠直接回收废电路板金属富集体中的铜[J].有色金属（冶炼部分）,2015(10):34-36.
Wang Zhi-ke,Wu Hai-li,Ye Cun-ling,Fan Shun-li.Direct Recovery of Copper from Metal Concentrates of Waste Printed Circuit Boards with Sodium Persulfate[J].Nonferrous Metals (Extractive Metallurgy),2015(10):34-36.
关注微信公众号