中文摘要: 以电弧炉炼锡产生的废渣为原料，盐酸为浸出剂，在温度40 ℃、液固比25︰1(mL/g)、搅拌速度250 r/min的条件下进行锡的富集。废渣中的锡含量由1.82%富集到13.61%，富集后的废渣再经酸浸、锌置换处理后，最终获得纯度98%的金属锡，锡回收率达99.5%，硅组分和钙组分的脱除率分别达到83.42%和94.21%，可以作为副产物出售，实现二次资源化。
Abstract:Tin was enriched from tin-smelting waste slag in electric arc furnace with hydrochloric acid as leaching agent under the conditions including temperature of 40 ℃, ratio of liquid to solid of 25︰1(mL/g), and stirring rate of 250 r/min. The results show that tin content in slag is enriched from 1.82% to 13.61%, and metal tin with purity of 98% is recovered with tin recovery of 99.5% from enriched slag by further acid-leaching and zinc replacement. The removal rate of silica and calcium, which can be sold as by-products, is 83.42% and 94.21% respectively.
keywords: tin-smelting waste slag tin recycling acid leaching
文章编号： 中图分类号： 文献标志码：
基金项目:国家科技支撑计划项目（2014BAC03B06）；江苏省科技支撑计划项目（BE2012645）
| 作者 | 单位 | |
| 于聪 | 江苏理工学院 | gjslab@163.com |
| 童霏 | 江苏理工学院 | |
| 王慧慧 | 江苏理工学院 | |
| 孙杨铖 | 江苏理工学院 | |
| 葛明敏 | 江苏理工学院 | |
| 周全法* | 江苏理工学院 | gjslab@163.com |
引用文本：
于聪,童霏,王慧慧,孙杨铖,葛明敏,周全法.炼锡废渣中锡的湿法富集工艺研究[J].有色金属（冶炼部分）,2015(7):17-20.
Yu Cong,Tong Fei,Wang Huihui,Sun Yangcheng,Ge Mingmin,Zhou Quanfa.Study on Tin Enrichment by Wet Process from Tin-smelting Waste Slag[J].Nonferrous Metals (Extractive Metallurgy),2015(7):17-20.
于聪,童霏,王慧慧,孙杨铖,葛明敏,周全法.炼锡废渣中锡的湿法富集工艺研究[J].有色金属（冶炼部分）,2015(7):17-20.
Yu Cong,Tong Fei,Wang Huihui,Sun Yangcheng,Ge Mingmin,Zhou Quanfa.Study on Tin Enrichment by Wet Process from Tin-smelting Waste Slag[J].Nonferrous Metals (Extractive Metallurgy),2015(7):17-20.
关注微信公众号