中文摘要: 通过模拟实际溶液与工业现场取样对比分析，探究湿法炼锌过程溶液中钙、镁的结晶机理。结果表明，溶液温度的降低是钙、镁结晶析出的主导因素；溶液中镁离子可诱导主金属元素锌的结晶析出；溶液中钙离子与镁离子在结晶析出过程中存在高盐分作用下的竞争反应，高温下溶液中钙离子易于镁离子优先结晶析出，低温下溶液中镁离子易于钙离子结晶析出。
Abstract:Crystallization mechanism of calcium and magnesium in zinc hydrometallurgy process was investigated by simulation of actual solution and field sampling comparative analysis. The results show that drop of solution temperature is the dominant factor in crystallization of calcium and magnesium. Magnesium ions in solution can induce crystallization precipitation of main metal element zinc. There is competing reaction between calcium and magnesium ions under high salinity in process of crystallization. Calcium ion is easy to be preferentially crystallized than magnesium ions in solution at high temperature while magnesium ions is easy to be preferentially crystallized than calcium ions in solution at low temperature.
文章编号： 中图分类号： 文献标志码：
基金项目:国家自然科学基金面上项目（51374167）
| 作者 | 单位 | |
| 高建雄 | 西安建筑科技大学冶金工程学院 | gjx420255765@126.com |
| 李林波* | 西安建筑科技大学冶金工程学院 | linboli73@126.com |
| 方钊 | 西安建筑科技大学冶金工程学院 | |
| 孔海林 | 西安建筑科技大学冶金工程学院 | |
| 薛宁 | 西安建筑科技大学冶金工程学院 |
| Author Name | Affiliation | |
| gao jian xiong | gjx420255765@126.com | |
| li lin bo | linboli73@126.com | |
| fang zhao | ||
| kong hai lin | ||
| xue ning |
引用文本：
高建雄,李林波,方钊,孔海林,薛宁.湿法炼锌过程钙镁结晶机理研究[J].有色金属（冶炼部分）,2015(7):1-4.
gao jian xiong,li lin bo,fang zhao,kong hai lin,xue ning.Crystallization Mechanism of Calcium and Magnesium in Zinc Hydrometallurgy Process[J].Nonferrous Metals (Extractive Metallurgy),2015(7):1-4.
高建雄,李林波,方钊,孔海林,薛宁.湿法炼锌过程钙镁结晶机理研究[J].有色金属（冶炼部分）,2015(7):1-4.
gao jian xiong,li lin bo,fang zhao,kong hai lin,xue ning.Crystallization Mechanism of Calcium and Magnesium in Zinc Hydrometallurgy Process[J].Nonferrous Metals (Extractive Metallurgy),2015(7):1-4.
关注微信公众号