中文摘要: 采用电化学溶解法对含Co、Cr、Al、W、Mo、Hf等金属的镍基高温合金废料在硫酸中的溶解过程进行研究。考察了电流密度、电解液酸度、温度、电解液Ni2+浓度对电解过程的影响。结果表明，在阳极电流密度300 A/m2、硫酸浓度1 mol/L、电解液温度40 ℃的条件下平均槽电压为2.4 V，电解1 t合金的能耗为2 083 kWh，电流效率98.46%。与硫酸体系相比，盐酸体系下稀散金属能在阳极泥中得到更好的富集。
Abstract:Dissolution process of Co, Cr, W, Al, Mo and Hf bearing nickel-base superalloy scraps in sulfuric acid solution was studied by electrochemical dissolution. The effects of current density, acidity, temperature and Ni2 concentration on electrochemical dissolution were investigated. The results show that the average cell voltage is 2.4 V and energy consumption is 2 083 kWh with current efficiency of 98.46% for one ton alloy scraps under the optimum conditions including current density of 300 A/m2, H2SO4 acidity of 98 g/L, and temperature of 40 ℃. Scattered metals can get higher enrichment in anode slime in hydrochloric acid system than in sulfuric acid system.
文章编号： 中图分类号：TF803.27 文献标志码：
基金项目:国家高技术研究发展计划（863计划）项目（2012AA063204）
| 作者 | 单位 | |
| 李波 | 西安建筑科技大学冶金工程学院 | yvfei1988@126.com |
| 朱军 | 西安建筑科技大学冶金工程学院 | |
| 李进 | 西安瑞鑫科金属金属材料有限公司 | |
| 许万祥 | 西安瑞鑫科金属金属材料有限公司 | |
| 郭瑞 | 西北有色金属研究院 |
| Author Name | Affiliation | |
| Li Bo | Xi’an University of Architecture & Technology | yvfei1988@126.com |
| Zhu Jun | ||
| Li Jin | ||
| Xu Wan-xiang | ||
| Guo Rui |
引用文本：
李波,朱军,李进,许万祥,郭瑞.电化学溶解镍基高温合金废料的研究[J].有色金属（冶炼部分）,2015(5):51-54.
Li Bo,Zhu Jun,Li Jin,Xu Wan-xiang,Guo Rui.Study on Electrochemical Dissolution of Nickel Base Superalloy Scraps[J].Nonferrous Metals (Extractive Metallurgy),2015(5):51-54.
李波,朱军,李进,许万祥,郭瑞.电化学溶解镍基高温合金废料的研究[J].有色金属（冶炼部分）,2015(5):51-54.
Li Bo,Zhu Jun,Li Jin,Xu Wan-xiang,Guo Rui.Study on Electrochemical Dissolution of Nickel Base Superalloy Scraps[J].Nonferrous Metals (Extractive Metallurgy),2015(5):51-54.
关注微信公众号