中文摘要: 在热力学分析的基础上，通过碳热还原和磁选分离对白云鄂博含铌尾矿中铁的回收与铌的富集进行探索性研究。结果表明，在1 000~1 100 ℃下，以碳为还原剂进行焙烧可以对含铌尾矿中的铁氧化物进行选择性还原。1 100 ℃焙烧0.5 h并经湿磨后在50 mT的磁场强度下磁选，可实现铁精粉与含铌矿物的分离。磁选所得铁精粉中铁品位为84.82%，铁收得率为81.95%，磁选尾矿中铌品位为1.98%，铌回收率达到95%以上。
Abstract:Iron recovery and niobium enrichment from Nb-bearing tailings in Bayan Obo were investigated by carbothermic reduction and magnetic separation based on thermodynamic analysis. The results show that iron oxide can be selective reduced at 1 000~1 100 ℃ with carbon as reductant. Separation of iron concentrate and niobium minerals could be realized by reduction roasting at 1 100 ℃ for 0.5 h and then wet grinding under magnetic field strength of 50 mT. Iron grade in magnetite iron concentrate is 84.82% with iron recovery rate of 81.95%. Nb2O5 grade in magnetic tailings is 1.98% with niobium recovery rate of 95% above.
文章编号： 中图分类号： 文献标志码：
基金项目:国家科技支撑计划项目（2008BAB32B07）
| 作者 | 单位 | |
| 张训迪 | 东北大学 多金属共生矿生态化冶金教育部重点实验室 | xundi_zhang@163.com |
| 刘承军* | 东北大学 多金属共生矿生态化冶金教育部重点实验室 | liuchengjun2008@163.com |
| 喻竹英 | 东北大学 多金属共生矿生态化冶金教育部重点实验室 | |
| 原浩植 | 东北大学 多金属共生矿生态化冶金教育部重点实验室 |
引用文本：
张训迪,刘承军,喻竹英,原浩植.含铌尾矿中铁与铌的分离与回收[J].有色金属（冶炼部分）,2015(2):5-8.
ZHANG Xun-di,LIU Cheng-jun,YU Zhu-ying,YUAN Hao-zhi.Separation and Recovery of Iron and Niobium from Nb-bearing Tailings[J].Nonferrous Metals (Extractive Metallurgy),2015(2):5-8.
张训迪,刘承军,喻竹英,原浩植.含铌尾矿中铁与铌的分离与回收[J].有色金属（冶炼部分）,2015(2):5-8.
ZHANG Xun-di,LIU Cheng-jun,YU Zhu-ying,YUAN Hao-zhi.Separation and Recovery of Iron and Niobium from Nb-bearing Tailings[J].Nonferrous Metals (Extractive Metallurgy),2015(2):5-8.
关注微信公众号