中文摘要: 以电煅煤、沥青焦、熟碎为骨料，改质沥青和煤焦油为粘结剂制备铝电解用炭间糊，并研究粘结剂含量对炭间糊性能的影响。结果表明，随着粘结剂含量的增加，炭间糊的挥发分增加；灰分、膨胀/收缩率先减小后增大，而体积密度、电阻率和耐压强度则是先增大后减小。当粘结剂含量为17%时炭间糊的综合性能最佳。
Abstract:Ramming pastes were prepared with calcined anthracite coal, pitch coke, and baked scrap as aggregate, modified pitch and coal tar as binder. The effect of content of binder on properties of ramming paste for aluminum electrolysis was investigated. As the results indicate, volatile component increases with increasing content of binder, both ash content and expansion/shrinkage rate decrease first and then increase, and bulk density, resistivity and compressive strength increase first and then decrease. The optimal comprehensive properties of ramming paste are obtained with content of binder of 17%.
keywords: ramming paste binder expansion/shrink rate
文章编号： 中图分类号： 文献标志码：
基金项目:贵州省科学技术基金项目(黔科合J字[2013]2221号)；贵州省科技计划项目(黔科合高G字[2012]4002)；贵州省普通高等学校特色重点实验室建设项目(黔教合KY[2012]004号)
| Author Name | Affiliation | |
| YAO Zhen | College of Material and Civil Engineering,Guizhou Normal University | 13595147706@163.com |
| LIU Wei | ||
| LIU Jing |
引用文本：
姚桢,刘卫,刘静.粘结剂含量对铝电解用炭间糊性能的影响[J].有色金属（冶炼部分）,2014(7):17-21.
YAO Zhen,LIU Wei,LIU Jing.Effect of Content of Binder on Properties of Ramming Paste for Aluminum Electrolysis[J].Nonferrous Metals (Extractive Metallurgy),2014(7):17-21.
姚桢,刘卫,刘静.粘结剂含量对铝电解用炭间糊性能的影响[J].有色金属（冶炼部分）,2014(7):17-21.
YAO Zhen,LIU Wei,LIU Jing.Effect of Content of Binder on Properties of Ramming Paste for Aluminum Electrolysis[J].Nonferrous Metals (Extractive Metallurgy),2014(7):17-21.
关注微信公众号