中文摘要: 通过考察浸出温度及硫酸浓度对石煤提钒浸出的影响，研究了机械活化前后矿样的浸出动力学。结果表明，未活化矿样浸出表观活化能为23.49 kJ/mol，反应级数为2.34，矿样活化20 min后，浸出表观活化能降为16.85 kJ/mol，反应级数降至2.21。机械活化能够增强矿样的表面活性，降低浸出过程对温度和硫酸浓度的依赖。
Abstract:The leaching dynamics before and after mechanical activation were studied through investigating effects of leaching temperature and sulfuric acid concentration on vanadium extraction from stone coal. The results indicate that apparent activation energy for non activated ore is 23.49 kJ/mol and reaction series is 2.62, and the according parameters decrease to 16.85 kJ/mol and 2.17 after 20 min mechanical activation. Mechanical activation could contribute to increase of surface energy so as to reduce dependence of leaching process on temperature and acidity.
keywords: mechanical activation stone coal vanadium leaching kinetics
文章编号： 中图分类号： 文献标志码：
基金项目:“十二五”国家科技支撑计划重点项目(2011BAB05B01)
| 作者 | 单位 | |
| 刘娟* | 武汉科技大学资源与环境工程学院 武汉科技大学资源与环境工程学院 | Lydia.2007.1227@163.com |
| 张一敏 | 武汉科技大学资源与环境工程学院 | |
| 黄晶 | 武汉科技大学资源与环境工程学院 | |
| 刘涛 | 武汉科技大学资源与环境工程学院 | |
| 黄献宝 | 武汉科技大学资源与环境工程学院 | |
| 马浩 | 武汉科技大学资源与环境工程学院 |
引用文本：
刘娟,张一敏,黄晶,刘涛,黄献宝,马浩.机械活化强化石煤酸浸提钒的动力学研究[J].有色金属（冶炼部分）,2014(7):27-31.
Liu Juan,Zhang Yimin,Huang Jing,Liu Tao,Huang Xianbao,Ma Hao.Leaching Kinetics on Enhancing Process to Extract Vanadium from Stone Coal by Mechanical Activation[J].Nonferrous Metals (Extractive Metallurgy),2014(7):27-31.
刘娟,张一敏,黄晶,刘涛,黄献宝,马浩.机械活化强化石煤酸浸提钒的动力学研究[J].有色金属（冶炼部分）,2014(7):27-31.
Liu Juan,Zhang Yimin,Huang Jing,Liu Tao,Huang Xianbao,Ma Hao.Leaching Kinetics on Enhancing Process to Extract Vanadium from Stone Coal by Mechanical Activation[J].Nonferrous Metals (Extractive Metallurgy),2014(7):27-31.
关注微信公众号