中文摘要: 采用沸腾焙烧—酸浸—氰化工艺处理高铜金精矿。工业实践表明，对于铜品位7%~10%的金精粉，全流程铜的回收率达到97%，酸浸渣含铜低于0.3%，氰化金浸出率96.84%，银浸出率75.45%，烟气SO2总转化率平均98.74%，处理后的烟气SO2浓度0.061%。
Abstract:High-grade copper-bearing gold concentrate was treated by processes of fluidized sulfating roasting, acid leaching, and cyaniding leaching. The industrial practice shows that copper total recovery rate is 97%, copper in acid leaching slag is below 0.3%, gold and silver cyaniding leaching rate is 96.84% and 75.45%, the average total conversion rate of SO2 is 98.74%, and SO2 concentration in waste gas is 0.061% when the gold concentrate bearing 7%~10% copper is treated by the above processes.
keywords: high-grade copper-bearing gold concentrate fluidized roasting industrial practice cyaniding
文章编号： 中图分类号： 文献标志码：
基金项目:
| 作者 | 单位 | |
| 杨要峰 | 灵宝黄金股份有限公司黄金冶炼分公司 | zkj0315@aliyun.com |
| 宋耀远 | 灵宝黄金股份有限公司黄金冶炼分公司 | |
| 赵可江* | 灵宝黄金股份有限公司黄金冶炼分公司 | zkjly2@163.com |
| 闾娟莎 | 灵宝黄金股份有限公司黄金冶炼分公司 | |
| 邵志恒 | 灵宝黄金股份有限公司黄金冶炼分公司 |
| Author Name | Affiliation | |
| Yang Yaofeng | LingBao Gold comapany Ltd Gold Smeltery Filiale | zkj0315@aliyun.com |
| Song Yaoyuan | ||
| Zhao Kejiang | zkjly2@163.com | |
| Lv Juansha | ||
| Shao Zhiheng |
引用文本：
杨要峰,宋耀远,赵可江,闾娟莎,邵志恒.高铜金精矿沸腾焙烧工业实践[J].有色金属（冶炼部分）,2014(4):54-57.
Yang Yaofeng,Song Yaoyuan,Zhao Kejiang,Lv Juansha,Shao Zhiheng.Industrial Practice of Fluidized Roasting of High-grade Copper-bearing Gold Concentrate[J].Nonferrous Metals (Extractive Metallurgy),2014(4):54-57.
杨要峰,宋耀远,赵可江,闾娟莎,邵志恒.高铜金精矿沸腾焙烧工业实践[J].有色金属（冶炼部分）,2014(4):54-57.
Yang Yaofeng,Song Yaoyuan,Zhao Kejiang,Lv Juansha,Shao Zhiheng.Industrial Practice of Fluidized Roasting of High-grade Copper-bearing Gold Concentrate[J].Nonferrous Metals (Extractive Metallurgy),2014(4):54-57.
关注微信公众号