中文摘要: 采用酸浸—氰化工艺从某沸腾焙烧烟灰中浸出金、银、铜。结果表明，较优工艺为：酸浸硫酸浓度1.0 mol/L，液固比4∶1，反应温度90 ℃，反应时间4 h，搅拌速度300 r/min；氰化浸出反应液固比3∶1，氰化钠浓度0.2 %，pH 10~11，反应时间48 h，搅拌速度300 r/min。此条件下，金、银、铜的浸出率分别为97.16%、79.98%、96.04%。
Abstract:Gold, silver and copper were leached from fluidized-bed roasting ash by sulfuric acid leaching-cyaniding leaching process. The results show that the leaching rate of gold, silver and copper is 97.16%, 79.98% and 96.04% respectively under the following optimal conditions including sulfuric acid concentration of 1.0 mol/L, ratio of liquid to solid of 4∶1, temperature of 90 ℃, reaction time of 4 h and stirring speed of 300 r/min as well as ratio of liquid to solid of 3∶1, sodium cyanide concentration of 0.2%, pH value of 10~11, reaction time of 48 h and stirring speed of 300 r/min in cyaniding leaching.
文章编号： 中图分类号：TF815 文献标志码：
基金项目:国家自然科学基金资助项目(51164011)；福建省区域科技重大合作项目（2011H4025）
| 作者 | 单位 | |
| 曾斌* | 江西理工大学冶金与化学工程学院 | zengbin1101@163.com |
| 赖子球 | 紫金矿业集团股份有限公司 | |
| 王瑞祥 | 江西理工大学冶金与化学工程学院 | |
| 余攀 | 江西理工大学冶金与化学工程学院 |
| Author Name | Affiliation | |
| ZENG Bin | School of Metallurgical and Chemical Engineering,Jiangxi University of Science and Technology,Ganzhou | zengbin1101@163.com |
| LAI Zi-qiu | ||
| WANG Rui-xiang | ||
| YU Pan |
引用文本：
曾斌,赖子球,王瑞祥,余攀.沸腾焙烧烟灰浸出金、银、铜的试验研究[J].有色金属（冶炼部分）,2014(3):25-28.
ZENG Bin,LAI Zi-qiu,WANG Rui-xiang,YU Pan.Study on Leaching of Gold-Silver-Copper from Fluidized-bed Roasting Ash[J].Nonferrous Metals (Extractive Metallurgy),2014(3):25-28.
曾斌,赖子球,王瑞祥,余攀.沸腾焙烧烟灰浸出金、银、铜的试验研究[J].有色金属（冶炼部分）,2014(3):25-28.
ZENG Bin,LAI Zi-qiu,WANG Rui-xiang,YU Pan.Study on Leaching of Gold-Silver-Copper from Fluidized-bed Roasting Ash[J].Nonferrous Metals (Extractive Metallurgy),2014(3):25-28.
关注微信公众号