中文摘要: 模拟“熔池熔炼法从沉铁渣中回收铁”工艺的高温氧化脱硫阶段，考察了温度、气氛和冷却方式对沉铁渣脱硫程度及铁富集效果的影响。硫酸铁分解脱硫的热力学计算与热分析表明，硫酸铁分解脱硫的温度分别为780.0 ℃和875.2 ℃，热力学计算得到的相变温度、分解温度与热分析曲线的吸热峰位置、失重阶段相吻合。沉铁渣脱硫阶段的最佳工艺条件为：炉膛温度1 300 ℃，氧气气氛，水淬法冷却产物。此时沉铁渣的脱硫率为99.55%，铁在产物中的含量为37.92%。
Abstract:The effects of temperature, atmosphere and cooling on desulfurization and iron-enrichment were investigated by simulating oxidative desulfurization stage of recycling iron from iron-sinking slag by bath smelting. Thermodynamic calculation and thermoanalysis demonstrate that desulfurization temperatures of iron sulfate are 780 ℃ and 875.2 ℃, respectively, and phase transition temperatures from thermodynamic calculation are consistent with TG and DSC results. The desulfurization rate of iron-sinking slag is 99.55% and iron content is upgraded to 37.92% under the optimum conditions of furnace temperature of 1 300 ℃, oxygen atmosphere and water-quenching.
keywords: bath smelting iron-sinking slag desulphurization iron-enrichment thermodynamic calculation thermoanalysis
文章编号： 中图分类号：TF812 文献标志码：
基金项目:国家高技术研究发展计划(863计划)项目(2011AA061003)
| 作者 | 单位 | |
| 刘群 | 中南大学 化学化工学院 | liuqun5880@126.com |
| 谭军* | 中南大学 化学化工学院 | yytanjun@163.com |
| 陈启元 | 中南大学 化学化工学院 | |
| 廖舟 | 株洲冶炼集团股份有限公司 | |
| 张平民 | 中南大学 化学化工学院 | zhangpm1939@sina.com |
| 尹周澜 | 中南大学化学化工学院 |
引用文本：
刘群,谭军,陈启元,廖舟,张平民,尹周澜.沉铁渣回收利用中的脱硫试验研究[J].有色金属（冶炼部分）,2014(2):1-4.
LIU Qun,TAN Jun,CHEN Qi-yuan,LIAO Zhou,ZHANG Ping-min,Yin Zhou-lan.Study on Desulphurization in Iron-sinking Slag Recycling[J].Nonferrous Metals (Extractive Metallurgy),2014(2):1-4.
刘群,谭军,陈启元,廖舟,张平民,尹周澜.沉铁渣回收利用中的脱硫试验研究[J].有色金属（冶炼部分）,2014(2):1-4.
LIU Qun,TAN Jun,CHEN Qi-yuan,LIAO Zhou,ZHANG Ping-min,Yin Zhou-lan.Study on Desulphurization in Iron-sinking Slag Recycling[J].Nonferrous Metals (Extractive Metallurgy),2014(2):1-4.
关注微信公众号