中文摘要: 采用氯化焙烧工艺从硫铁矿烧渣球团中综合回收金、银、铜等有价金属，考察了造球、窑温、停留时间对金属挥发率以及物料和金属平衡的影响。结果表明，物料在1 250 ℃停留1.83 h的最佳条件下，各金属挥发率为：Au 95.6%、Ag 52.5%、Cu 73.1%、Pb 93.9%、Zn 75.2%。球团中铜、铅、锌含量均小于0.1%，球团强度4 0~6.5 kN。
Abstract:Valuable metals such as Au, Ag, and Cu were comprehensively recovered from pyrite cinder by chloridizing roasting process. The effects of pelletizing, roasting temperature and staying duration on metal volatilization rates and mass balance of materials and metals were investigated. The results show that the volatilization rates of Au, Ag, Cu, Pb, Zn are 95.6%, 52.5%, 73.1%, 93.9%, and 75.2% respectively under the optimum conditions including roasting temperature of 1 250 ℃ and staying duration of 1.83 h. The contents of Cu, Pb, Zn in chloridizing pellet are all below 0.1%, and the compression strength of pellet is 4 0~6.5 kN.
文章编号： 中图分类号： 文献标志码：
基金项目:国家高技术研究发展计划（863计划）项目（2011AA06A104）
| 作者 | 单位 | |
| 常耀超* | 北京矿冶研究总院冶金所 | chang_yc@bgrimm.com |
| 徐晓辉 | 北京矿冶研究总院冶金所 | |
| 王云 | 北京矿冶研究总院工程公司 |
| Author Name | Affiliation | |
| changyaochao | Beijing General Research Institute of Mining | chang_yc@bgrimm.com |
| xuxiaohui | ||
| wangyun |
引用文本：
常耀超,徐晓辉,王云.硫铁矿烧渣氯化焙烧扩大试验研究[J].有色金属（冶炼部分）,2013(10):1-3.
changyaochao,xuxiaohui,wangyun.Chloridizing Roasting Expanding Test of Pyrite Cinder[J].Nonferrous Metals (Extractive Metallurgy),2013(10):1-3.
常耀超,徐晓辉,王云.硫铁矿烧渣氯化焙烧扩大试验研究[J].有色金属（冶炼部分）,2013(10):1-3.
changyaochao,xuxiaohui,wangyun.Chloridizing Roasting Expanding Test of Pyrite Cinder[J].Nonferrous Metals (Extractive Metallurgy),2013(10):1-3.
关注微信公众号