中文摘要: 以氰尿酸、硝酸镧、氢氧化钠为原料合成了氰尿酸镧，采用正交试验法确定了合理的工艺条件。采用转矩流变仪研究与比较了氰尿酸镧、硬脂酸镧、硬脂酸钙、硬脂酸锌等热稳定剂对PVC的塑化作用。结果表明，氰尿酸镧的最佳合成工艺为70 ℃、氢氧化钠浓度1.2 mol/L、反应时间60 min、pH 7；氰尿酸类与硬脂酸类稀土稳定剂复合后对PVC的塑化效果最佳。
Abstract:Lanthanum cyanurate was synthesized from cyanuric acid, lanthanum nitrate and sodium hydroxide. The optimum synthesis conditions of lanthanum cyanurate were determined by orthogonal test. The plastication of lanthanum cyanurate, lanthanum stearate, calcium stearate and zinc stearate on PVC was investigated and compared with torque rheometer. The results show that the optimum synthesis conditions include temperature of 70 ℃, NaOH concentration of 1.2 mol/L, reaction time of 60 min, and pH of 7. The combination of rare earth cyanurate stabilizer and rare earth stearate stabilizer has the optimum plastication results.
keywords: PVC lanthanum cyanurate thermal stability plastication
文章编号： 中图分类号： 文献标志码：
基金项目:国家杰出青年基金项目(51045216)；长江学者和创新团队发展计划资助项目(50725416)；内蒙古自治区高等学校创新团队发展计划项目（NMGIRT1104）
| 作者 | 单位 | |
| 姜在勇* | 内蒙古科技大学材料与冶金学院 | zaiyong1108551@sina.com |
| 李 梅 | 内蒙古科技大学材料与冶金学院 | |
| 柳召刚 | 内蒙古科技大学材料与冶金学院 | |
| 胡艳宏 | 内蒙古科技大学材料与冶金学院 | |
| 王觅堂 | 内蒙古科技大学材料与冶金学院 | |
| 王海鸥 | 内蒙古科技大学材料与冶金学院 |
引用文本：
姜在勇,李 梅,柳召刚,胡艳宏,王觅堂,王海鸥.氰尿酸镧的最佳合成工艺及其对PVC塑化作用的研究[J].有色金属（冶炼部分）,2013(12):48-51.
jiangzaiyong,Jiang Zaiyong,Liu Zhaogang,Hu Yanhong,Wang Mitang,Wang Haiou.Study on Optimum Synthesis Process of Lanthanum Cyanurate and Its Plastication on PVC[J].Nonferrous Metals (Extractive Metallurgy),2013(12):48-51.
姜在勇,李 梅,柳召刚,胡艳宏,王觅堂,王海鸥.氰尿酸镧的最佳合成工艺及其对PVC塑化作用的研究[J].有色金属（冶炼部分）,2013(12):48-51.
jiangzaiyong,Jiang Zaiyong,Liu Zhaogang,Hu Yanhong,Wang Mitang,Wang Haiou.Study on Optimum Synthesis Process of Lanthanum Cyanurate and Its Plastication on PVC[J].Nonferrous Metals (Extractive Metallurgy),2013(12):48-51.
关注微信公众号