中文摘要: 研究了利用微波配碳还原焙烧分解铁酸锌的工艺及机理。利用碳气化控制、化学控制及扩散控制模型研究了样品中铁酸锌分解的动力学行为，并考察了微波功率、反应温度、配碳比和粒度对铁酸锌分解率的影响。结果表明，样品的微波加热碳热还原试验的控制步骤为碳气化控制，活化能为39.21 kJ/mol，在微波加热温度850 ℃、C/ZnFe2O4质量比为1∶4、粒径74~89 μm、微波功率1.8 kW、加热时间60 min的条件下，铁酸锌的分解率达到90%。
Abstract:The process and mechanism of carbothermic reduction with microwave of ZnFe2O4 were studied. The decomposition kinetics of ZnFe2O4 was carried out with models of carbon gasification, interfacial area of mass transfer, and diffusion control. The effects of microwave power, reaction temperature, ratio of C/ZnFe2O4, and particle size on decomposition rate of ZnFe2O4 were investigated. The results show that the controlling model of decomposition of ZnFe2O4 is carbon gasification control with the kinetics of ln(1-3α)=kt and activation energy of 39.21 kJ/mol. The decomposition rate of ZnFe2O4 is up to 90% under the conditions including microwave heating temperature of 850 ℃, mass ratio of C/ZnFe2O4 of 1/4, particle size of 74~89 μm, microwave power of 1.8 kW, and reaction time of 60 min.
keywords: kinetics zinc ferrite activation energy microwave mechanism
文章编号： 中图分类号： 文献标志码：
基金项目:国家自然科学基金资助项目(51104073)；云南省中青年学术技术带头人后备人才项目（2012HB008）
| Author Name | Affiliation | |
| WangXin | Kunming University of Science and Technology | wangxinwa84@163.com |
| YANG Da-jin | ||
| PENG Jin-hui | ||
| JV Shao-hua |
引用文本：
王欣,杨大锦,彭金辉,巨少华.微波加热配碳还原分解铁酸锌的工艺及机理研究[J].有色金属（冶炼部分）,2013(5):1-4.
WangXin,YANG Da-jin,PENG Jin-hui,JV Shao-hua.Carbothermic Process and Mechanism Study on Zinc Ferrite Decomposition with Microwave[J].Nonferrous Metals (Extractive Metallurgy),2013(5):1-4.
王欣,杨大锦,彭金辉,巨少华.微波加热配碳还原分解铁酸锌的工艺及机理研究[J].有色金属（冶炼部分）,2013(5):1-4.
WangXin,YANG Da-jin,PENG Jin-hui,JV Shao-hua.Carbothermic Process and Mechanism Study on Zinc Ferrite Decomposition with Microwave[J].Nonferrous Metals (Extractive Metallurgy),2013(5):1-4.
关注微信公众号