中文摘要: 针对某铜盐厂硫酸铜产品杂质钙含量较高的现状，选用P204从硫酸铜溶液中萃取钙。考察P204质量浓度、相比O/A、萃取时间、水相平衡pH等对铜钙萃取分离的影响。结果表明，P204萃取钙的适宜条件为：P204质量浓度1.2 mol/L，O/A=5∶1，振荡时间3 min，pH=1.5。四级逆流萃取后，水相中钙质量浓度低于0.05 g/L。
Abstract:P204 was chosen to extract calcium from copper sulfate solution, taking high calcium of impurities in copper sulfate products into consideration. The effects of P204 mass concentration, O/A, extraction time, and equilibrium pH value of aqueous phase on separation of copper and calcium were investigated. The results show that the optimum conditions of P204 extraction include P204 mass concentration of 0.9 mol/L, O/A=5∶1, oscillation time of 3 min, and pH value of 1.5. The calcium mass concentration in water phase is below 5 mg/L after 4-stage countercurrent extraction.
keywords: P204 extraction separation of copper and calcium countercurrent extraction copper sulfate solution
文章编号： 中图分类号： 文献标志码：
基金项目:
| 作者 | 单位 | |
| 朱军 | 西安建筑科技大学冶金工程学院 | zhujun_tiger@126.com |
| 许万祥* | 西安建筑科技大学冶金工程学院 | 15353572399@163.com |
| 洪涛 | 西安建筑科技大学冶金工程学院 | |
| 李志仁 | 西安建筑科技大学冶金工程学院 | |
| 卓文 | 金川公司铜盐厂 |
| Author Name | Affiliation | |
| ZhuJun | school of metallurgy,Xi’an University of Architecture and Technology,Xi’an | zhujun_tiger@126.com |
| XuWanxiang | 15353572399@163.com | |
| HonTao | ||
| LiZhiren | ||
| ZhuoWen |
引用文本：
朱军,许万祥,洪涛,李志仁,卓文.P204萃取硫酸铜溶液中的钙[J].有色金属（冶炼部分）,2013(5):13-16.
ZhuJun,XuWanxiang,HonTao,LiZhiren,ZhuoWen.Extraction of Calcium from Copper Sulfate Solution with P204[J].Nonferrous Metals (Extractive Metallurgy),2013(5):13-16.
朱军,许万祥,洪涛,李志仁,卓文.P204萃取硫酸铜溶液中的钙[J].有色金属（冶炼部分）,2013(5):13-16.
ZhuJun,XuWanxiang,HonTao,LiZhiren,ZhuoWen.Extraction of Calcium from Copper Sulfate Solution with P204[J].Nonferrous Metals (Extractive Metallurgy),2013(5):13-16.
关注微信公众号