中文摘要: 制备了赤泥富钛渣，并通过单因素和正交试验考查了硫酸浓度、反应时间、反应温度对二氧化钛酸解率的影响。结果表明，影响二氧化钛酸解率因素的主次顺序为硫酸浓度、反应温度和反应时间。较佳酸化条件是反应温度180 ℃、反应时间140 min和硫酸浓度95%，二氧化钛酸解率为96.32%。
Abstract:The Ti-enriched slag was prepared, and the influence of sulfuric acid concentration, reaction time and reaction temperature on acidolysis rate of titanium dioxide were studied by single factor and orthogonal experiment. The results show that the factors sequenced according to the significant level were sulfuric acid concentration, reaction temperature and reaction time. The optimum acidification conditions include the reaction temperature of 180 ℃, reaction time of 140 min, and the sulfuric acid concentration of 95%, under these conditions, the acidolysis rate of titanium dioxide reaches 96.32%.
keywords: red mud Ti-enriched slag leaching sulfuric acid
文章编号： 中图分类号： 文献标志码：
基金项目:贵州省基金项目（黔科合J字[2009]2057号）；贵阳市科技局项目（[2010]筑科Ⅰ合同字第1-76号、筑科合同[2011205]5-7号）
| 作者 | 单位 | |
| 宋强 | 贵州大学 | mm.qs@gzu.edu.cn |
| 王家伟* | 贵州大学 | w_j_wei@qq.com |
| 徐本军 | 贵州大学 |
| Author Name | Affiliation | |
| Song Qiang | Guizhou University | mm.qs@gzu.edu.cn |
| Wang Jiawei | w_j_wei@qq.com | |
| Xue Benjun |
引用文本：
宋强,王家伟,徐本军.硫酸浸出赤泥富钛渣[J].有色金属（冶炼部分）,2012(5):27-29.
Song Qiang,Wang Jiawei,Xue Benjun.Leaching of Ti-enriched Slag from Red Mud with Sulfuric Acid[J].Nonferrous Metals (Extractive Metallurgy),2012(5):27-29.
宋强,王家伟,徐本军.硫酸浸出赤泥富钛渣[J].有色金属（冶炼部分）,2012(5):27-29.
Song Qiang,Wang Jiawei,Xue Benjun.Leaching of Ti-enriched Slag from Red Mud with Sulfuric Acid[J].Nonferrous Metals (Extractive Metallurgy),2012(5):27-29.
关注微信公众号