中文摘要: 结合铅富氧闪速熔炼的特点，对相关渣型进行了研究。结果表明，适当提高炉渣的CaO含量，可有效降低渣含铅。适宜的渣型为FeO/SiO2 =1.15、CaO/SiO2=0.6，炉渣的熔点和黏度均可满足熔炼要求。
Abstract:The slag types were studied based on the characteristics of lead oxygen-enriched flash smelting process. The results show that the lead content in the slag decrease effectively with the increasing of CaO content in the slag. The optimum slag is FeO/SiO2 =1.15, CaO/SiO2=0.6, of which the melting point and viscosity can meet the smelting demands.
文章编号： 中图分类号： 文献标志码：
基金项目:国家高技术研究发展计划（863计划）资助项目(2009AA064602)
| Author Name | Affiliation |
| YIN Fei, WANG Cheng-yan, WANG Zhong, GAO Wei, LI Qiang | Beijing General Research Institute of Mining and Metallurgy, Beijing 100070, China |
引用文本：
尹飞，王成彦，王忠，郜伟，李强.铅富氧闪速熔炼技术基础研究[J].有色金属（冶炼部分）,2012(4):11-14.
YIN Fei, WANG Cheng-yan, WANG Zhong, GAO Wei, LI Qiang.Basic Research on Lead Oxygen-Enriched Flash Smelting Technology[J].Nonferrous Metals (Extractive Metallurgy),2012(4):11-14.
尹飞，王成彦，王忠，郜伟，李强.铅富氧闪速熔炼技术基础研究[J].有色金属（冶炼部分）,2012(4):11-14.
YIN Fei, WANG Cheng-yan, WANG Zhong, GAO Wei, LI Qiang.Basic Research on Lead Oxygen-Enriched Flash Smelting Technology[J].Nonferrous Metals (Extractive Metallurgy),2012(4):11-14.
关注微信公众号