中文摘要: 蒸发冷凝技术制备了平均直径为80 nm的铅粉,反应完成后冷却至室温,通入一定浓度氧气的惰气原位对所制备的纳米铝粉进行钝化,采用XRD,TEM,XPS和HRTEM检测钝化后的纳米铝粉颗粒及表面的化学成分、形貌和结构.结果表明钝化后的纳米铝颗粒为表面形成厚度小于5 nm的致密的钝化膜包覆着金属铝的"核壳"结构.结合晶体结构推断纳米铝颗粒的钝化过程分为三个阶段:第一阶段受隧道效应的控制,反应非常快,氧化层迅速增厚,第二阶段随氧化膜增厚,离子流下降很快,倾斜场的协同效应导致膜生长变慢,速度控制步骤仍然是隧道效应,第三阶段热电子流起主要作用,氧化膜的生长几乎停止.
Abstract:Aluminum nanoparticles with average diameter of 80 nm were prepared by evaporation-condensation method.After preparation,the powder was passivatedin situby inert gas containing a little of oxygen. XRD,TEM,XPS and HRTEM were employed to investigate the chemical component,shape and structure of the nanoparticles and its surface.It shows that the structure of the passivated particle presents acore-shellconformation with a oxide overlayer less than 5 nm thickness enwraping aliuminum metal. The structural analys...
keywords: Evaporation-condensation method Nanophased aluminum Oxidation membrane Passivation machenism
文章编号： 中图分类号：TG174.4 文献标志码：
基金项目:
MA Jiang-hong YU Yue-guang WANG Lei LIU Jian-ping
MA Jiang-hong~1,YU Yue-guang~1,WANG Lei~1,LIU Jian-ping~2 (1.Beijing General Research Institute of Mining & Metallurgy,Beijing 100044,China,2.Military Representatives in Liming Company,Shenyang 110043,China)
引用文本：
马江虹,于月光,王磊,刘建平.纳米铝粒子表面钝化过程研究[J].有色金属（冶炼部分）,2008(Z1):.
.Process of Aluminum Nanoparticles Surface Passivation[J].Nonferrous Metals (Extractive Metallurgy),2008(Z1):.
马江虹,于月光,王磊,刘建平.纳米铝粒子表面钝化过程研究[J].有色金属（冶炼部分）,2008(Z1):.
.Process of Aluminum Nanoparticles Surface Passivation[J].Nonferrous Metals (Extractive Metallurgy),2008(Z1):.
关注微信公众号