超音速火焰喷涂Cr_3C_2-25%NiCr涂层的滑动摩擦磨损性能研究

Study on Sliding Wear Behavior of 25%NiCr-Cr_2C_3 Coatings Sprayed by HVOF

摘要

图/表

参考文献

相似文献

本文已被：浏览 2925次下载 28次

中文摘要: 采用超音速火焰喷涂工艺制备了Cr3C2-25%NiCr陶瓷,对涂层的组织结构、显微硬度及在滑动摩擦条件下的失重进行了分析,得出了涂层摩擦因数与时间的关系,对涂层的滑动摩擦磨损机理进行了分析.结果表明Cr3C2-25%NiCr涂层致密,孔隙率为0.96%,涂层截面的显微硬度平均值HV0.3为867.涂层稳定的摩擦因数为0.1.初始阶段涂层的磨损主要是磨屑对涂层的磨粒磨损作用,摩擦稳定后涂层的磨损主要是由于相对运动面的磨削作用.

中文关键词: 超音速火焰喷涂Cr3aC2-25％NiCr 涂层滑动摩擦

Abstract:Cr_3C_2-25%NiCr coatings were prepared on No.45 steel substrate by means of high velocity oxyfuel spraying(HVOF).Coating porosity,microhardness and weightness loss of coating in the sliding wear test were studied.Profiles of the sliding wear coefficients were described and the wear mechanisms of coatings were discussed as well.The results show that the coatings are compact with the porosity of 0.96%,and the hardness of the coatings is 867 HV under the loading of 300 gram.Abrasion of the coatings is stable a...

keywords: High Velocity Oxy-Fuel Spraying(HVOF) Cr_3C_2-25%NiCr Coating Sliding wear

文章编号： 中图分类号：TG174.44 文献标志码：

基金项目:

高峰刘富荣任先京北京矿冶研究总院;

GAO Feng LIU Fu-rong REN Xian-jing GAO Feng,LIU Fu-rong,REN Xian-jing (Beijing General Institute of Mining , Metallurgy,Beijing 100044,China)

引用文本：
高峰,刘富荣,任先京.超音速火焰喷涂Cr_3C_2-25%NiCr涂层的滑动摩擦磨损性能研究[J].有色金属（冶炼部分）,2008(Z1):.
.Study on Sliding Wear Behavior of 25%NiCr-Cr_2C_3 Coatings Sprayed by HVOF[J].Nonferrous Metals (Extractive Metallurgy),2008(Z1):.