中文摘要: 采用等离子弧堆焊技术,在Q235钢表面堆焊镍基合金粉末,通过工艺试验、硬度试验、磨损试验和显微组织观察分析,研究了等离子弧堆焊层的常规性能.试验结果表明镍基合金粉末堆焊层硬度和耐磨性较基体有显著提高.
Abstract:Nickel-based alloy powder was deposited on the surface of Q235 steel by plasma-arc surfacing,the convention performance of plasma-arc surfacing is studied by process test,hardness test,wearing test and microstructure observation and analysis.The results indicate that the hardness and wear resistance of deposited layers of nickel-based alloy powder increased evidently compared with the substrate.