中文摘要: 分析比较了常规大气等离子喷涂、爆炸喷涂和超音速火焰喷涂的WC／Co涂层的形貌、显微组织、孔隙率、硬度、结合强度及其耐磨性。结果表明，超音速火焰喷涂和爆炸喷涂层性能相当，涂层具有与粉末相近的相结构，与大气等离子喷涂相比，涂层具有高的致密度、硬度和良好的耐磨性，涂层与基体的结合情况也得到很大的改善。
Abstract:The micrograph,microstructure,porosity,hardness,bond strength and wear resistance of WC/Co coatings deposited with plasma spraying,detonation spraying and high velocity oxy-fuel(HVOF) thermal spraying.The results show that the phase of HVOF and Detonation WC/Co coating is much the same as the WC/Co powder.The WC/Co coatings deposited with HVOF and Detonation spraying has higher density,hardness and wear resistance,and the combining of the coating and substrate was greatly improved.
文章编号： 中图分类号：TB333 文献标志码：
基金项目:
引用文本：
鲍君峰,于月光,刘海飞,曾克里,任先京.三种热喷涂工艺制备WC/Co涂层性能比较[J].有色金属（冶炼部分）,2006(4):46-49.
.Comparison of Properties of WC/Co Coating Prepared by Three Kinds of Thermal Spraying Process[J].Nonferrous Metals (Extractive Metallurgy),2006(4):46-49.
鲍君峰,于月光,刘海飞,曾克里,任先京.三种热喷涂工艺制备WC/Co涂层性能比较[J].有色金属（冶炼部分）,2006(4):46-49.
.Comparison of Properties of WC/Co Coating Prepared by Three Kinds of Thermal Spraying Process[J].Nonferrous Metals (Extractive Metallurgy),2006(4):46-49.
关注微信公众号