中文摘要: 对FeO—Si02-MgO-CaO渣系的电导率进行了测试研究。结果表明，在CaO6％，Fe／SiO2=1．2时，随着MgO含量的增加，熔渣电导率增大。MgO11％，Fe／SiO2=1．2时，电导率随CaO含量的增加而增大，当CaO含量大于6％，CaO含量的变化对电导率的影响较弱。电导率随Fe／SiO2比值增加而增大。温度增加，熔渣电导率增大。
中文关键词: 炉渣 电导率 FeO—MgO-CaO—SiO2系
Abstract:The electrical conductivity of molten FeO-MgO-CaO-SiO_2 semi-synthetic slags for nickel flash smelting are measured. The results show that the electrical conductivity of molten slag increase with increasing MgO content at CaO content of about 6% and Fe to SiO_2 ratio of about 1.2. When CaO content is below 6%, the electrical conductivity increase with the increase of CaO at MgO content of 11% and Fe to SiO_2 ratio of about 1.2. However, when CaO content is more than 6%, the conductivity increase slightly for FeO-MgO-CaO-SiO_2 system. It is also found that the electrical conductivity of the melts increase with increasing temperature and higher Fe to SiO_2 ratio.
文章编号： 中图分类号：TF815 文献标志码：
基金项目:
引用文本：
戴曦,张传福.FeO-MgO-CaO-SiO2系炉渣电导的测定与研究[J].有色金属（冶炼部分）,2005(4):2-4.
.Electrical Conductivity Measurement of FeO-MgO-CaO-SiO2 Slag[J].Nonferrous Metals (Extractive Metallurgy),2005(4):2-4.
戴曦,张传福.FeO-MgO-CaO-SiO2系炉渣电导的测定与研究[J].有色金属（冶炼部分）,2005(4):2-4.
.Electrical Conductivity Measurement of FeO-MgO-CaO-SiO2 Slag[J].Nonferrous Metals (Extractive Metallurgy),2005(4):2-4.
关注微信公众号